Investigation of He-W interactions using DiMES on DIII-D

Abstract

Tungsten button samples were exposed to He ELMing H-mode plasma in DIII-D using 2.3 MW of electron cyclotron heating power. Prior to the exposures, the W buttons were exposed to either He, or D, plasma in PISCES-A for 2000 s at surface temperatures of 225-850 °C to create a variety of surfaces (surface blisters, subsurface nano-bubbles, fuzz). Erosion was spectroscopically measured from each DiMES sample, with the exception of the fuzzy W samples which showed almost undetectable WI emission. Post-exposure grazing incidence small angle x-ray scattering surface analysis showed the formation of 1.5 nm diameter He bubbles in the surface of W buttons after only a single DIII-D (3 s, ∼150 ELMs) discharge, similar to the bubble layer resulting from the 2000 s. exposure in PISCES-A. No surface roughening, or damage, was detected on the samples after approximately 600 ELMs with energy density between 0.04-0.1 MJ m-2. Show more